Multi-Material Processing: Hybrid Disk-Shaped Parts Wrought AA6061 & AM-SLM AlSi10Mg
Keywords:
AM-SLM, AlSi10Mg, wrought 6061, hybrid parts, interface characterizationAbstract
Multi-material processing was successfully carried out for AA6061 aluminum wrought alloy and AlSi10Mg for SLM to produce hybrid components. The interface formed during the SLM process was analyzed at the bonding zone between the two materials. Preliminary investigation revealed that a good metallurgical bonding was obtained at the boundary created between the AA6061 aluminum wrought alloy and AlSi10Mg AM-SLM material. This was validated by ultrasonic testing and observed by optical and electron microscopy. As expected, a highly refined microstructure was obtained due to rapid solidification during SLM and the macrostructure was not changed at the interface following solidification, bonding and a T5 heat treatment. Microhardness results show that the interface exhibited different values than the bulk materials stemming from the chemical mixing that occurred during melting. This work showed the feasibility of creating hybrid components combining additive manufacturing with conventional fabrication methods.
Downloads
Downloads
Published
Issue
Section
License
Papers accepted for publication become the copyrighted property of the Annals of "Dunarea de Jos" University of Galati, Fascicle XII, Welding Equipment and Technology. No part of the publication may be reproduced or transmitted in any form, or by any means, electronic or mechanical, including photocopy, recording, or any information storage and retrieval system, except in limited quantities for the non-commercial purposes of scientific or educational advancement, without permission in writing from the Editorial Board.